Influencia de la fibra de caña seca y húmeda en un 3% adicionada a un concreto convencional, comparando la resistencia a compresión y tensión indirecta
dc.contributor.advisor | Gálvez Bohórquez, Melisa | spa |
dc.contributor.author | Baquero Mora, Luz Adriana | spa |
dc.contributor.author | Briceño Ruiz, Lisbeth Daniela | spa |
dc.date.accessioned | 2019-12-17T20:48:01Z | |
dc.date.available | 2019-12-17T20:48:01Z | |
dc.date.issued | 2019-12-13 | spa |
dc.identifier.uri | http://hdl.handle.net/11396/5635 | |
dc.description | Basados en la implementación de fibras naturales en la construcción y aprovechamiento del desecho de la fibra de la caña de azúcar, el presente proyecto analiza el comportamiento mecánico a compresión y tensión indirecta, por medio de tipologías propuestas, con base en el método que establece Diego Sánchez De Guzmán, se realiza un respectivo diseño de mezcla para una resistencia de 3000 psi, tomando como asentamiento una consistencia media siendo de 5 a 10 cm, resultados obtenidos con los ensayos de densidad del cemento, densidad y absorción, masa unitaria y granulometría para los agregados finos y gruesos. Se ejecutaron 12 especímenes cilíndricos de (10 cm) 4” de diámetro y (20 cm) 8” de longitud, divididos en 3 tipologías, 4 cilindros para la muestra patrón, 4 cilindros compuestos de las fibras de caña de azúcar seca catalogada como mezcla (tipo 1), se realiza un secado previo a las fibras secas, estas son expuestas al sol durante 5 días, 4 cilindros compuestos de la fibra de caña de azúcar con el contenido de humedad natural (tipo 2), la fibra será añadida al compuesto cilíndrico en un 3% con respecto al peso del cemento, a los 7 y 14 días de proceso de curado. Se realizan los respectivos cálculos para comparan las tipologías de mezcla, sometiendo 2 cilindros de muestra patrón, 2 cilindros Tipo 1, 2 cilindros Tipo 2, al ensayo de resistencia a la compresión de cilindros normales de concreto regido por la NTC 673 y esta misma división de especímenes cilíndricos a el ensayo para determinar la resistencia a la tensión indirecta de especímenes cilíndricos de concreto regido por la NTC 722. Con base en estos resultados se reconoce que la fibra de caña en el concreto minimiza su peso y así mismo su densidad, donde la fibra seca se comporta mejor en resistencia compresión que la fibra humedad y en el ensayo de tensión indirecta se comporta mejor la fibra humedad que la fibra seca, pero estas no se comportan mejor que la muestra patrón | spa |
dc.description.abstract | Based on the implementation of natural fibers in the construction and use of sugarcane fiber waste, this project analyzes the mechanical behavior of compression and indirect tension, through proposed typologies, based on the method established by Diego Sánchez De Guzmán, a respective mix design for a resistance of 3000 psi is carried out, taking as a settlement a medium consistency being 5 to 10 cm, results obtained with the tests of cement density, density and absorption, unit mass and grain size for thin and thick aggregates. Twelve cylindrical specimens of (10 cm) 4 ”in diameter and (20 cm) 8” in length were executed, divided into 3 typologies, 4 cylinders for the standard sample, 4 cylinders composed of the fibers of dry sugarcane classified as a mixture (type 1), a pre-drying is done to the dry fibers, these are exposed to the sun for 5 days, 4 cylinders composed of the sugar cane fiber with the natural moisture content (type 2), the fiber will be added to the 3% cylindrical compound with respect to the weight of the cement, at 7 and 14 days of curing process, the respective calculations are made to compare the types of mixing, submitting 2 cylinders of standard sample, 2 cylinders Type 1, 2 cylinders Type 2, to the compressive strength test of normal concrete cylinders governed by NTC 673 and this same division of cylindrical specimens to the test to determine the indirect tensile strength of cylindrical specimens of concrete governed by NTC 722. Based on these results, it is recognized that cane fiber in concrete minimizes its weight and density, where dry fiber behaves better in compressive strength than moisture fiber and in the test of Indirect tension behaves better than moisture fiber than dry fiber, but these do not behave better than the standard sample | spa |
dc.language.iso | spa | spa |
dc.publisher | Universidad La Gran Colombia | spa |
dc.rights | Attribution-NonCommercial-NoDerivatives 4.0 International | * |
dc.rights.uri | http://creativecommons.org/licenses/by-nc-nd/4.0/ | * |
dc.subject | Fibras de bagazo de caña de azúcar | spa |
dc.subject | Diseño de mezcla | spa |
dc.subject | Ensayo de agregados | spa |
dc.subject | Inmunización de fibras naturales. | spa |
dc.subject | Ensayo de compresión | spa |
dc.subject | Ensayo de tensión indirecta | spa |
dc.subject | Concreto reforzado con fibras | spa |
dc.title | Influencia de la fibra de caña seca y húmeda en un 3% adicionada a un concreto convencional, comparando la resistencia a compresión y tensión indirecta | spa |
dc.subject.lemb | Compuesto fibroso - caña de azúcar | spa |
dc.subject.lemb | Materiales de construcción - compuesto fibroso | spa |
dc.subject.lemb | Hormigón | spa |
dc.subject.lemb | Agregados (materiales de construcción) - caña de azúcar | spa |
dc.subject.lemb | Caña de azúcar - pruebas mecánicas | spa |
dc.publisher.department | Facultad de Arquitectura | spa |
dc.publisher.program | Tecnología en Construcciones Arquitectónicas | spa |
dc.subject.keyword | Sugar cane bagasse fibers | spa |
dc.subject.keyword | Mix design | spa |
dc.subject.keyword | Aggregate test | spa |
dc.subject.keyword | Immunization of natural fibers | spa |
dc.subject.keyword | Compression test | spa |
dc.subject.keyword | Indirect tension test | spa |
dc.subject.keyword | Fiber reinforced concrete | spa |
dc.coverage.sede | Bogotá | spa |
dc.creator.degree | Tecnólogo(a) en Construcciones Arquitectónicas | spa |
dc.contributor.manager | Gavilanes, José Dario | spa |